EMULSOL PV-9
(TU 2422-171-00209556-2003)
EMULSOL PV-9 is a water solution mixture of polyethylene glycols, surfactants and corrosion inhibitors, easily soluble in water. For its properties and application it is similar to liquid coolants of “Ecol” type. It shows high cooling and oiling effect. Does not cause corrosion. It is neither inflammable nor explosive. It is not volatile. It does not render harmful influence on skin and respiratory tract. The concentrate and working solutions are stable, do not stratify. It is easily dosed. It is applied in form of 3÷10% water solutions.
Technical Characteristics
Parameters
| Standard |
Hydrogen parameter, рН |
9-11 |
Density at 20ºС, kg/m3 |
1000-1100 |
Freezing point, ºС |
-13÷-15 |
Application
It is applied as oil-free cooling mixture at various ways of metal working: cutting, milling, grinding, thread milling, drilling, etc.
EMULSOL 22
(TU 6-13-00209556-145-98). The Sanitary-and-epidemiologic certificate №77 99 98025 Д 0110691008 from October 15, 2008.
The composition is on the base of coal oil, nonionic surfactants, and corrosion inhibitor. It shows high cooling and oiling effect. Shows high cooling and greasing ability. Does not cause corrosion. It is not volatile. It does not render harmful influence on skin and respiratory tract. It is applied in form of 2-10 % water emulsions.
Technical Characteristics
Parameters |
Standard |
Hydrogen parameter of 5% water emulsion, рН |
7,2-8,5 |
Density at 20ºС, kg/m3 |
0,88-0,95 |
Application
It is applied as cooling mixture at various ways of metal working (drilling, milling, etc.)
MOLD OIL МV-2 (Type B)
(TU 2484-136-00209556-97)
It is a coal oil water emulsion containing emulsifier and corrosion inhibitor. MOLD OIL МV-2 practically does not colour concrete, does not reduce its strength. The surface of concrete becomes smooth, polished, the number of surface pores decreases. The preparation is fireproof, non- toxic, harmless for human skin, economic in application (rate of application is 1,5-2 times less compared to standard oils and makes 100-110 g/m2). Oiling of the surface is done with the help of a brush or by mechanisms.
Technical Characteristics
Parameters |
Standard |
Hydrogen parameter, рН |
10,5-12,0 |
Density at 20ºС, kg/m3 |
940-980 |
Application
It is applied as oil for compression molds at manufacturing of different concrete and ferro-concrete products.
Water-soluble varnish VRL-1
(TU 6-13-00209556-94-92)
Water-soluble varnish VRL-1 is a water solution mixture of polyethylene glycols, an organic polyacid, isopropyl alcohol. Limitless miscibility with water. Does not freeze up to-20 0С. The rate of application is 2-3 times less compared to standard varnishes of Hv-784, 5179, NC-134I type. It is easily washed off by water. The varnish is easily applied on metal half-finished products by any way: with the help of a brush, rollers, spray gun, resulting in uniform covering which protects pressed parts and half-finished products from damages at cutting and perforation of metal, allows to avoid machining burrs. It is used undiluted. The shelf life is 1 year.
Technical Characteristics
Parameters |
Standard |
Contents of nonvolatile substances, % |
20 |
Congelation point, ºС, below |
-20 |
Drying time (on air), min |
30 |
Application
It is applied as a temporary covering for metal surface protection against damages at cold pressing, cutting and perforation of metal. Can be used as sheeting instead of paper for plexiglas during its transportation and storage.
|